Abstrakt

Ceramic electrolytes based on Yb and Sc stabilized zirconia enable efficient heat transfer and effective ionic conductivity. Here, the design and synthesis of Yb and Sc stabilized zirconia electrolyte is presented for intermediate temperature solid oxide fuel cells (SOFCs). Yb0.12Sc0.08Zr0.8O2–δ was synthesized using the sol-gel method, and a thorough characterization of the electrolyte properties was conducted including structural and electrical properties. X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDS) confirmed the composition of the electrolyte. A single-phase cubic structure with a density of 6.7041 ± 0.0008 g cm−3 was obtained. The thermal expansion coefficient in the temperature range from 25 °C to 800 °C is equal to 1.17 × 10−6 K−1. The activation energy of 1.06 eV and 1.15 eV was obtained for the bulk and grain boundary conductivity, respectively. The ionic conductivity of approx. 2.10 S m−1 was achieved at 667 °C, thus it is suitable for efficient ionic conduction at intermediate temperatures.